Copper Nickel Alloy Strip Monel 400 for Nuclear Industry

Model NO.: Monel 400
Yield Strength: >170 MPa
Tensile Strength: > 480 MPa
Elongation in 2 in.: > 35%
Chemical Composition: Cu, Ni
Trademark: Ualloy
Specification: RoHS, SGS
Origin: Zhejiang, China
HS Code: 74122010
Characteristic as below
      Monel 400 is an extremely combination property that use for largest amount and most widely corrosion resistance alloy. This alloy in the hydrofluoric acid and fluoride gas medium with excellent corrosion resistance, as well as to the hot concentrated alkali. At the same time, is also corrosion resistant to neutral solution, sea water, air, organic compounds. An important feature of this is generally do not generate a stress corrosion cracking, good cutting performance.
 
Monel 400 Metallurgical structure
      Monel 400 alloy is high-intensity single-phase solid solution.
 
Monel 400 Corrosion resistance
      Monel 400 alloy in the fluoride gas, hydrochloric acid, sulfuric acid, hydrofluoric acid and their derivatives have a very good corrosion resistance property, and possess better corrosion resistance more than the copper alloy in the sea water. Acid medium: Monel 400 have corrosion resistance in less than 85% consistency of sulfuric acid. Monel 400 is an important material that resistant to hydrofluoric acid. Water corrosion: Monel 400 alloy in most corrosion cases of water, not only excellent corrosion resistance, but also less pitting, stress corrosion, the corrosion rate less than 0.025mm / a. High temperature corrosion: Monel 400 for the work of the highest temperature at about 600 °C in general in the air, in the high temperature steam, the corrosion rate less than 0.026mm / a. Ammonia: Monel 400 can be resistant to an hydrous ammonia and aminate conditions corrosion below 585 °C due to the high nickel. 
 
 
1. Description
 
Monel is a series of nickel alloys, primarily composed of nickel (up to 67%) and copper, with some iron and other trace elements.  
 
       Chemical Content(%)
Mn Ni Cu C Si P S Fe
2 Bal <34 <0.3 0.5   <0.025 2.5
 
        Mechanical Properties
 
Density 8.83 g/cm3
Melting Range 1300-1390 ºC
Yield Strength >170 Mpa
Tensile Strength > 480 Mpa
Elongation in 2 in. > 35%

2.size
   Strip: Thickness: 0.01mm-3.0mm
       Width: 0.5mm-200mm

3. Usage
 
Monel 400 alloy is a multi-purpose material in many industrial applications: 

(1. Seamless water pipe in the power factory 
(2. Sea-water exchanger and evaporator 
(3. Sulfuric acid and hydrochloric acid environment 
(4. Crude distillation 
(5. Sea-water in the use of equipment and propeller shaft 
(6. Nuclear industry and used in the manufacture of uranium enrichment isotope separation equipmen(7. Manufacturing hydrochloric acid equipment used in the production of pump and valve. 
 
4. Packing detail
 
 1) Coil (plastic spool) + compressed ply-wooden case + pallet 
 2) Coil (plastic spool) + carton + pallet  
 
5. Products and services
 
1). Pass: ISO9001 certification, and SO14001cetification;
2). Fine after-sale services;
3). Small order accepted;
4). Fast delivery;

6.Inspection and Test Procedure
1.100% PMI,Spectro Chemical Aanlysis Test for Raw Material
2.100% Dimension & Visual Examination 
3. Mechanical Properties Test Include Tension Test,Flaring Test (For Seamless tube/pipe)/ Flange Test (For Welded Pipe & Tube), Hardness Test ,Reversed Flattening Test
4.100% Hydrostatic Test or 100% NON-DESTRUCTIVE Test  (ET or UT) 
5.Radiographic Test for Welded Pipe (shall be accordance with specification,or shall be as agreed upon between the purchaser and vendor)
6.Straightness Test  (optional)
7.Roughness Test (optional)
8.Intergranular Corrosion Test(optional)
9.Impact Test (optional)
10.Grain Size Determinations (optional)
NOTES : ALL THE TESTS AND INSPECTION RESULT NEED TO BE SHOWED IN REPORTS ACCORDING TO STANDARD AND SPECIFICATION.
 

Eyebolts And Eyenuts

Eye Nuts,Eye Bolts Screwfix,Eyebolts And Eyenuts,Stainless Steel Eye Bolts

Jiangsu Hongze Stainless Steel Wire Rope Co., Ltd , https://www.hzrope.com